logo

EZHOU ANJEKA TECHNOLOGY CO.,Ltd Anjeka@anjeka.net 86-0711-5117111

Home
Products

Polymeric Dispersing Agent

Pigment Dispersing Agent

Nanoparticle Dispersion

Paint Dispersing Agent

Wetting And Dispersing Agent

Waterborne Pigment Dispersant

Levelling Agent

Anti Settling Agent

Thixotropic Agent

Defoamer Additive

Adhesion Promoter

General Purpose Dispersant

Water Based Paint Additives

Oil Based Paint Additives

Polyethylene Wax Dispersion
Videos
About Us
Company Profile
Factory Tour
Quality Control
Contact Us
News
Cases
english
français
Deutsch
Italiano
Русский
Español
português
Nederlandse
ελληνικά
日本語
한국
Get Best Price Quote
Home
Products

Polymeric Dispersing Agent

Pigment Dispersing Agent

Nanoparticle Dispersion

Paint Dispersing Agent

Wetting And Dispersing Agent

Waterborne Pigment Dispersant

Levelling Agent

Anti Settling Agent

Thixotropic Agent

Defoamer Additive

Adhesion Promoter

General Purpose Dispersant

Water Based Paint Additives

Oil Based Paint Additives

Polyethylene Wax Dispersion
Videos
About Us
Company Profile
Factory Tour
Quality Control
Contact Us
News
Cases
EZHOU ANJEKA TECHNOLOGY CO.,Ltd company profile
Cases
Home > Cases >
Company Cases About The thickening effect of modified polyurea thixotropic agent on PVC paste resin system

The thickening effect of modified polyurea thixotropic agent on PVC paste resin system

2026-01-10
Latest company cases about The thickening effect of modified polyurea thixotropic agent on PVC paste resin system

The thickening effect of modified polyurea thixotropic agent on PVC paste resin system

Test Formulation
Raw material Amount      
PVC resin paste 100      
thixotropic agent 0.6      
Experimental Procedure

1.Begin by subjecting the paste to high-speed dispersion at 4000 rpm for 25 minutes, until the paste temperature reaches 60°C.

2.Then let it stand for 15 minutes

 

3.Finally, add the thixotropic agent, disperse at 1500R/min for 10 minutes, and then take it out

 

4.Measure the viscosity and measure the viscosity after 24 hours

Result

 

 Anjeka4410 Anjeka4410S Competitive product 410 Blank

Initial viscosity

(25℃mpa.s)

> 2 million

Pasty / non-flowing

> 2 million

Pasty / non-flowing

 1 million
 4,800

Viscosity after 24 hours

(25℃mpa.s)

> 2 million

Pasty / non-flowing

> 2 million

Pasty / non-flowing

> 2 million

Pasty / non-flowing

 4,800
Conclusion Test results indicate that the modified polyurea thixotropic agent from Anjeka provides a superior thickening effect in PVC paste resin slurry, outperforming competitive products which exhibited less effective thickening on the same day.

 

latest company case about The thickening effect of modified polyurea thixotropic agent on PVC paste resin system 0

High-viscosity paste with viscosity exceeding 2 million centipoise, exhibiting a non-flowing consistency.

Events

News

Cases
Contacts
Contacts: Ms. Anna
Tel: 86-0711-5117111
Fax: 86-0711-3809626
Contact Now
Mail Us
About US
Company Profile
Factory Tour
Quality Control
Contact Us
SiteMap
Privacy Policy
products

Polymeric Dispersing Agent

Pigment Dispersing Agent

Nanoparticle Dispersion

Paint Dispersing Agent

Wetting And Dispersing Agent

Waterborne Pigment Dispersant

Contact UsEZHOU ANJEKA TECHNOLOGY CO.,Ltd
Anjeka@anjeka.net
86-0711-5117111
R&D Center:Building 19, Phase III, Gaoxin Smart City, Gedian Development Zone Ezhou City, Hubei Province China
linkedin facebook twitter
China Good Quality Polymeric Dispersing Agent Supplier. Copyright © 2024-2026 EZHOU ANJEKA TECHNOLOGY CO.,Ltd . All Rights Reserved.